![]() It should be noted that it is a very fluid resin so when applied on vertical surfaces it can drip. Jewelry and small pieces of no more than 5x5x5 cm. When to use Translux D151 Fast resin for 24 hours of curing? ![]() To make tables, do not exceed 2cm in height per casting. If the encapsulation is larger, it is advisable to do it in layers since the more volume, the more risk of yellowing it has. if they are higher than this there is a possibility that it will deform since there is contraction.Įncapsulations of no more than 10x10x10. When to use the standard Translux D150 resin of 72 hours of curing?Ĭastings greater than 1 centimeter thick and minimum of 2.5. Ultra 4 Epoxy Parafilm.Īs we said before, Translux D150 resin has two catalyst possibilities and now we are going to explain in which cases it is recommended to use one or the other. This particular release agent is specially formulated for epoxy resins on silicone molds. If working on silicone or rubber molds, it is advisable to use a release agent since due to the slow curing and overexposure in the mold, it can dry out and deteriorate very quickly. The plastic should never touch the resin. If you are going to do several castings because the thickness of the work requires it, it is advisable to cover the work with a clean plastic to prevent dust particles from depositing on the surface and spoiling the effect. When these machining processes are done, never do it at maximum revolutions, since you run the risk of spoiling the result in the same way. These times are always variable depending on the ambient temperature. If you do it before, you run the risk of the sandpaper being soaked or the resin being melted. But apart from the recommended curing times, you will have to wait 2 or 3 more days in the case of the Translux D151 and 4 extra days in case it is the translux D150 to be able to do it. Once you notice that the resin is fluid again, shake the bottle well so that all the components of the container are well mixed. In winter, due to the cold, part A is usually gelled so it is advisable to heat it inside its container in the water bath or bringing it closer to an indirect heat source. Varying the percentage of catalyst by increasing it, will make it lose this quality and be left with a slight yellowish tone. ![]() This means that it resists UV rays and takes longer to yellow than a polyester resin or an epoxy resin that does not have this quality. The translux D150 is a completely transparent resin with UV filter. Varying the percentage of catalyst will make the resin not cure, take longer to cure, be rubbery, burn, etc. The mixing ratio is 2:1 in weight, so you have to put twice as much A as B. This resin, like almost all of them, is composed of two components, Part A D150 ( base ) and Part B D150 or D151 ( catalyst ). The best tips to achieve an optimal result with Translux D150andnbsp epoxy resin We know that this is very difficult and that is why we are going to give you some tips to make the result as perfect as possible. If we work below this temperature it will take longer to cure and, if we exceed these marks, the process can be accelerated too much and even burned. The ideal is to work them at a stable temperature of between 20º and 24º. That is, in general, all resins, whether epoxy, polyester or polyurethane are affected by temperature. Meet the two versions of Translux D150 epoxy resinĪ slow one whose curing time can be extended up to 72 hours.ĭespite these indications, you should keep in mind that curing times can be affected depending on how and where they are being used. Therefore, in this article Feroca, we will summarize what possibilities it has, the warnings of its use, qualities and other tips so that you can get the most out of this resin and obtain the best results. Allowing it to be applied in laminate, in casting, with pigments, fillers and more. This transparent epoxy resin is very versatile, since it offers a multitude of applications and possibilities when working with it.
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |